Korozija betonskih stupova armiranih različitim vrstama čelika nakon dugotrajnog izlaganja realnom morskom okolišu

diplomski rad

• Naslov (engleski): Corrosion of concrete columns with different steel reinforcement after long-term exposure to real marine environment
• Autor: Eva Zimprich
• Mentor: Marijana Serdar (mentor)
• Član povjerenstva: Marijana Serdar (predsjednik povjerenstva)
• Član povjerenstva: Marijan Skazlić (član povjerenstva)
• Član povjerenstva: Nina Štirmer (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Građevinski fakultet; (Zavod za materijale); Zagreb
• Datum i država obrane: 2022-09-29, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Građevinarstvo

Sažetak

Korozija čelika najčešći je uzrok prijevremenog propadanja i skraćivanja uporabnog vijeka armiranobetonskih konstrukcija. Ogromni troškovi i sigurnosna pitanja povezana s korozijom čelika u betonu rezultirala su razvojem širokog spektra tehnologija i materijala kako bi se povećala trajnost armiranobetonskih konstrukcija. Jedna od metoda, kojima se odgađa ili u potpunosti sprječava pojava korozije, je korištenje određenih vrsta korozijski otpornih čelika s nižim udjelom legirajućih elemenata, koji su otporniji na koroziju od ugljičnog čelika, dok im je cijena značajno niža od nehrđajućih čelika. Cilj ovog rada bio je provesti analizu korozijskog procesa na armiranobetonskim stupovima koji su 10 godina bili izloženi realnom morskom okolišu podno Krčkog mosta. Stupovi su bili armirani različitim vrstama čelika, a svaki stup se sastojao od 2 šipke od ugljičnog čelika i 2 šipke od korozijski otpornih čelika. U radu su provedena ispitivanja na ukupno pet vrsta armaturnih čelika: na ugljičnom čeliku (B500B), na feritnom čeliku (TOP12), austenitnom čeliku s većim udjelom nikla (304L), austenitnom čeliku s manjim udjelom nikla (204Cu), dvije vrste dupleks čelika (1.4362, 2205). Na pojedinoj vrsti čelika analizirao se korozijski proces s ciljem istraživanja utjecaja vrste legura na dugotrajno ponašanje čelika u morskom okolišu. Također je bilo potrebno ustanoviti utjecaj nehrđajuće armature na brzinu korozije obične armature od ugljičnog čelika, kada se iste nalaze unutar betonskog stupa. Istraživanja u ovom radu provedena su uz pomoć optičkog 3D skenera, kojim je omogućeno automatizirano analiziranje korozijskih napada na različitim vrstama čelika.

Sažetak (engleski)

Steel corrosion is the most frequent cause of early deterioration and shortening of service life of reinforced concrete structures. Huge costs and safety issues related to steel corrosion in concrete resulted in development of a wide range of technologies and materials in order to increase the durability of reinforced concrete structures. One of the methods, which delay or fully prevent corrosion, is the use of certain types of corrosion resistant steel with lower alloying elements, which are more corrosion resistant than carbon steel, while their price is significantly lower than stainless steel. The aim of this thesis was to analyse the corrosion process on reinforced concrete columns that were exposed for 10 years to the real marine environment below the Krk bridge. The columns were reinforced with different types of steel, and each column consisted of 2 carbon rebars and 2 corrosion-resistant rebars. Tests were carried out on total of five types of reinforcing steel: carbon steel (B500B), ferritic steel (TOP12), austenitic steel with higher nickel content (304L), austenitic steel with lower nickel content (204 Cu), and two types of duplex steel (1.4362, 2205). The corrosion process was analyzed on a particular type of steel with the aim of investigating the influence of the type of alloy on the long-term behavior of steel in the marine environment. It was also necessary to establish the influence of stainless steel reinforcement on the corrosion rate of ordinary carbon steel reinforcement, when it is placed inside the same concrete column. The research in this work was carried out with the help of an optical 3D scanner, which enabled the automated analysis of corrosion attacks on different types of steel.

• Ključne riječi: Korozija; korozijski otporni armaturni čelici; morski okoliš; smanjenje promjera armature; 3D skener
• Ključne riječi (engleski): corrosion; corrosion resistant steel; marine environment; loss of cross section; 3D scanner
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:237:214049
• Studijski program: Naziv: Građevinarstvo; smjerovi: Organizacija građenja, Prometnice, Geotehnika, Hidrotehnika, Konstrukcije, Materijali, Teorija i modeliranje konstrukcija; Smjer: Organizacija građenja; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka građevinarstva (mag. ing. aedif.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Zatvoreni pristup
• Datum i vrijeme pohrane: 2023-01-30 10:31:03