Utjecaj udjela i duljine otpadnih staklenih vlakana na svojstva morta

diplomski rad

• Naslov (engleski): Influence of proportion and length of waste glass fibres on cement mortar properties
• Autor: Lucija Holub
• Mentor: Ana Baričević (mentor)
• Član povjerenstva: Ivana Banjad Pečur (predsjednik povjerenstva)
• Član povjerenstva: Ana Baričević (član povjerenstva)
• Član povjerenstva: Marija Jelčić Rukavina (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Građevinski fakultet; (Zavod za materijale); Zagreb
• Datum i država obrane: 2023-02-16, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Građevinarstvo

Sažetak

U sklopu diplomskog rada provedena su istraživanja utjecaja udjela i duljine otpadnih alkalno-otpornih staklenih vlakana (AR-GF) na svojstva morta. Korištena otpadna vlakna nastaju tijekom proizvodnje tehničkih tekstila za građevinski sektor. Takva vlakna nisu pogodna za daljnju primjenu te su za rad dodatno obrađena prije primjene. Vlakna su rezana na duljinu 5 i 10 mm, a za ocjenu doprinosa svojstvima morta korištena su u četiri volumna udjela: 0.2%, 0.4%, 0.6% i 0.8%. Provedena su ispitivanja utjecaja otpadnih AR-GF na svojstva u svježem i očvrsnulom stanju. Rezultati ukazuju na otpadna AR-GF vlakna ne doprinose povećanju vlačne i tlačne čvrstoće, kao ni duktilnosti ispitanih mortova. Istovremeno, pozitivan doprinos se ogleda u smanjenom autogenom skupljanju, u odnosu na referentnu mješavinu i tvornički proizvedena AR-GF vlakna, a što je primarni razlog primjene ovih vlakana u mortu visoke čvrstoće.

Sažetak (engleski)

In this master thesis, the influence of the proportion and length of alkali-resistant glass fibres from production (AR-GF) on the properties of cement mortar was investigated. The waste fibres used are produced during the production of technical textiles for the construction sector. These fibres are not suitable for further use and were additionally prepared for this work before use. The fibres were cut to lengths of 5 and 10 mm and used in four volume proportions to evaluate the contribution to the properties of the cement mortar: 0.2%, 0.4%, 0.6% and 0.8%. The tests on the influence of the waste fibres AR-GF were carried out in the fresh and hardened state. The results show that the waste fibres AR-GF do not contribute to the increase of tensile and compressive strength and ductility of the tested mortars. At the same time, the positive contribution is reflected in lower autogenous shrinkage compared to the reference mix and the factory-produced AR-GF fibres, which is the accepted reason for using these fibres in high-strength mortars.

• Ključne riječi: otpadna staklena vlakna; mort visoke čvrstoće; skupljanje
• Ključne riječi (engleski): waste glass fibres; high strength mortar; shrinkage
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:237:077345
• Studijski program: Naziv: Građevinarstvo; smjerovi: Organizacija građenja, Prometnice, Geotehnika, Hidrotehnika, Konstrukcije, Materijali, Teorija i modeliranje konstrukcija; Smjer: Organizacija građenja; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka građevinarstva (mag. ing. aedif.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Zatvoreni pristup
• Datum i vrijeme pohrane: 2023-03-16 10:06:35