Veziva na bazi kalcinirane gline u betonima široke primjene

diplomski rad

• Naslov (engleski): Binders based on calcined clay in concrete of wide application
• Autor: Alma-Dina Bašić
• Mentor: Marijana Serdar (mentor)
• Član povjerenstva: Ana Baričević (predsjednik povjerenstva)
• Član povjerenstva: Marija Jelčić Rukavina (član povjerenstva)
• Član povjerenstva: Marijana Serdar (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Građevinski fakultet; (Zavod za materijale); Zagreb
• Datum i država obrane: 2020-09-24, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Građevinarstvo

Sažetak

Razvojem infrastrukture u cijelom svijetu povećava se potražnja za cementnim materijalima. Unatoč poboljšanju procesa proizvodnje cementa u okoliš se otpušta znatna količina CO 2 . Upotreba mineralnih dodataka kao zamjena za dio cementnog klinkera je rješenje za smanjenje emisije CO 2 u okoliš, a da se pritom zadrže istovjetna mehanička i trajnosna svojstva betona. Količine mineralnih dodataka, koji su se do sada najviše koristili, nisu dovoljne za sve veće potrebe cementne industrije. Glina koja sadrži kaolin dostupna je u zemljama gdje se očekuje najveća potreba za cementom. Kalciniranjem postiže pucolanska svojstva, a u kombinaciji s vapnencem smanjuje troškove proizvodnje i negativan utjecaj na okoliš. U ovom radu dio cementa je zamijenjen kombinacijom kalcinirane gline i vapnenca. Provedena su ispitivanja betona ciljanih čvrstoća C25/30 i C30/37. Ispitana su svojstva mješavina u svježem i očvrsnulom stanju. Moguće je postići zahtijevana svojstva betona običnih čvrstoća dodatkom kalcinirane gline i vapnenca sa smanjenjem negativnog utjecaja na okoliš.

Sažetak (engleski)

With the development of infrastructure all over the world, the demand for cementitious materials is increasing. Despite the improvement of the cement production process, a significant amount of CO 2 is released into the environment. The use of supplementary cementitious materials (SCM) to replace part of the clinker in cement is a solution for reducing CO 2 emissions into the environment, while maintaining the same mechanical and durable properties of concrete. The quantities of SCMs, which have been used the most, are not sufficient for the growing needs of the cement industry. Clays containing kaolinite are available in countries where the greatest need for cement is expected. By calcination it achieves pozzolanic properties and in combination with limestone it reduces production costs and negative impact on the environment. In this research, part of the cement has been replaced by a combination of calcined clay and limestone. Tests of concrete of target strengths C25/30 and C30/37 were performed. The properties of fresh and hardened mixtures were examined. It is possible to achieve the required properties of ordinary strength concrete by addition of calcined clay and limestone with a reduction of negative impact on the environment.

• Ključne riječi: cement; kalcinirana glina; vapnenac; emisija CO 2; mehanička svojstva; svojstva trajnosti
• Ključne riječi (engleski): cement; calcined clay; limestone; CO 2 emissions; mechanical properties; durabilitiy properties
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:237:174534
• Studijski program: Naziv: Građevinarstvo; smjerovi: Organizacija građenja, Prometnice, Geotehnika, Hidrotehnika, Konstrukcije, Materijali, Teorija i modeliranje konstrukcija; Smjer: Organizacija građenja; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka građevinarstva (mag. ing. aedif.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Zatvoreni pristup
• Datum i vrijeme pohrane: 2023-06-06 08:36:17