UTJECAJ POLIURETANSKE PJENE NA PONAŠANJE LAGANIH KOMPOZITNIH PANELA U POŽARNIM UVJETIMA

diplomski rad

• Naslov (engleski): THE INFLUENCE OF POLYURETHENE FOAMS ON THE BEHAVIOR OF LIGHTWEIGHT COMPOSITE PANELS IN FIRE CONDITIONS
• Autor: Antonija Ivanović
• Mentor: Marija Jelčić Rukavina (mentor)
• Član povjerenstva: Marija Jelčić Rukavina (predsjednik povjerenstva)
• Član povjerenstva: Marijana Serdar (član povjerenstva)
• Član povjerenstva: Marijan Skazlić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Građevinski fakultet; Zagreb
• Datum i država obrane: 2023-09-28, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Građevinarstvo

Sažetak

Osnovni cilj ovog diplomskog rada je, na temelju eksperimentalnog ispitivanja, procijeniti utjecaj poliuretanske pjene na ponašanje laganih kompozitnih panela u požarnim uvjetima. Zbog toga je ispitana otpornost na požar dvaju uzorka laganih kompozitnih panela koji su se sastojali od čeličnog okvira i sa po dva sloja gips-vlaknastih ploča s obje strane. Jedan uzorak je sadržavao poliuretansku pjenu kao toplinsko-izolacijski sloj, dok je drugi (referentni) bio prazan. Kroz ispitivanje je praćen razvoj temperatura kroz presjek panela te parametri kojima se dokazuje nosivost, izolacija i cjelovitost kod standardiziranog ispitivanja otpornosti na požar konstrukcijskih elemenata. Dodatno je provedena termogravimetrijska analiza korištene PUR pjene. Dobiveni rezultati pokazuju da gorivost poliuretanske pjene smanjuje otpornost na požar panela, ali se korištenjem više slojeva gips-vlaknastih ploča može osigurati otpornost panela od najmanje 60 minuta.

Sažetak (engleski)

The energy efficiency requirements of buildings force an increased use of thermal insulation materials in buildings, which can be of inorganic or organic origin, i.e., non-combustible or combustible. The main objective of this work is to evaluate, through experimental tests, the influence of polyurethane foam (PUR) on the behavior of lightweight composite panels under conditions of high fire temperatures. For this reason, the fire resistance of two specimens of lightweight composite panels consisting of a steel frame and two layers of gypsum fiberboard was tested. One specimen contained PUR foam as a thermal insulation layer, while the other (reference) was blank. During the test, the temperature evolution in the cross-section of the panel was monitored, as well as the parameters to demonstrate the load-bearing capacity, insulation and integrity of the standardized fire resistance test of building components. In addition, a thermogravimetric analysis of the PUR foam used was performed. The results obtained show that the flammability of the polyurethane foam reduces the fire resistance of the panel, but the use of multiple layers of gypsum fiberboard can ensure the resistance of the panel of at least 60 minutes.

• Ključne riječi: lagani kompozitni paneli; gips-vlaknaste ploče; poliuretanska pjena; otpornost na požar
• Ključne riječi (engleski): light weight composite panels; gypsum-fiber boards; polyurethane foam; fire resistance
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:237:884475
• Studijski program: Naziv: Građevinarstvo; smjerovi: Organizacija građenja, Prometnice, Geotehnika, Hidrotehnika, Konstrukcije, Materijali, Teorija i modeliranje konstrukcija; Smjer: Organizacija građenja; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka građevinarstva (mag. ing. aedif.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Zatvoreni pristup
• Datum i vrijeme pohrane: 2023-10-25 08:01:21